Mahendra Kumar Trivedi, Rama Mohan Tallapragada, Alice Branton, Dahryn Trivedi, Gopal Nayak, Rakesh Kumar Mishra et Snehasis Jana
Neopentyl glycol (NPG) has been extensively used as solid-solid phase change materials (PCMs) for thermal energy storage applications. The objective of the present study was to evaluate the impact of biofield treatment on physical, spectral and thermal properties of NPG. The study was performed in two groups (control and treated). The control group remained as untreated, and treatment group was subjected to Mr. Trivedi’s biofield treatment. The control and treated NPG were characterized by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and Fourier transform infrared (FT-IR) spectroscopy. XRD study revealed the decrease in crystallite size of treated NPG by 21.97% as compared to control sample. DSC studies showed slight change in melting temperature of treated NPG as compared to control sample. TGA analysis showed 55.66% weight loss in control NPG however, the treated sample showed reduction in weight loss (44.81%). Additionally, the maximum thermal decomposition temperature (Tmax) of treated NPG (160.40°C) was minimally increased with respect to control sample (159.72ºC). This can be inferred as good thermal stability of biofield treated NPG with respect to control. FT-IR spectroscopy showed no structural changes in treated NPG with respect to control sample. The overall results showed that biofield treatment has affected the physical and thermal properties of treated NPG.